    • Taendl, Johannes
    • Poletti, Cecilia
  • TitelInfluence of \(Al_3(Sc,Zr)\) Precipitates on Deformability and Friction Stir Welding Behavior of Al-Mg-Sc-Zr Alloys
  • Datei
  • DOI10.1007/s00501-016-0504-4
  • Persistent Identifier
  • Erschienen inBHM Berg- und Hüttenmännische Monatshefte
  • Band161
  • Erscheinungsjahr2016
  • Heft7
  • Seiten330-333
  • ISSN1613-7531
  • ZugriffsrechteCC-BY
  • Download Statistik1399
  • Peer ReviewNein
  • AbstractWe investigate the influence of \(Al_3(Sc,Zr)\) precipitates on the cold deformability and friction stir welding behavior of a novel AlMg4Sc0.4Zr0.12 alloy. To analyze the influence of the precipitate state on the flow stress, samples were pre-aged at various temperatures for up to 120 min prior to plane strain compression. It was found that the flow stress increased considerably with increasing pre-ageing temperature and duration. The formation of \(Al_3(Sc,Zr)\) precipitates during friction stir welding was investigated on welds with high and low heat input by measuring the respective hardening response with and without post-weld heat treatment.